Microwave properties of YBCO/LAO and YBCO/MgO superconducting thin films;
YBCO/LAO和YBCO/MgO超導(dǎo)薄膜的微波性質(zhì)
Effect of Tl_2O partial pressure on component phases and properties of Tl_2Ba_2CaCu_2O_8 superconducting thin films fabricated at lower temperature in pure argon atmosphere;
低溫純Ar氣中Tl_2O分壓對Tl_2Ba_2CaCu_2O_8超導(dǎo)薄膜相組成與性能的影響
High T_c superconducting thin film of YBa_2Cu_3O_(7-x) and Zro_2 buffer layer have been de-posited in situ on(100)silicon substrate with excimer laser.
利用ＺｅＣｌ準(zhǔn)分子激光在（１００）Ｓｉ基片上原位淀積出ＺｒＯ＿２緩沖層和ＹＢａ＿２Ｃｕ＿３Ｏ＿（７－ｘ）高Ｔ＿ｃ超導(dǎo)薄膜，薄膜的零電阻溫度為８２Ｋ。
The results shown that the superconducting films were polycrystalline with stronger c-axis texture.
對多層蒸鍍經(jīng)高溫退火制備的T_c≥83K的超導(dǎo)薄膜進(jìn)行了XRD及EPMA研究。
Hollow cylindrical cathode, dc magnetron sputtering method was used to fabricate the YBCOsuperconducting films on LaAlO_3 and Zr(Y)O_2 substrate.
采用中空柱狀陰極直流磁控濺射裝置制備了YBCO超導(dǎo)薄膜。
In Situ annealed superconducting thin films are acquired by pulsed laser deposition method.
采用脈沖激光沉積的方法在Al2O3(0001)基片上先生成MgB混和薄膜,然后采用原位后退火的方法生成MgB2超導(dǎo)薄膜,采用磁測量(MT)、X射線衍射、掃描電子顯微鏡技術(shù)分析了各種沉積及退火條件對MgB2超導(dǎo)薄膜表面形貌、晶體結(jié)構(gòu)、超導(dǎo)電性的影響。
The most promising application of high-TC superconducting thin films is passive microwave devices and the fabrication of large-area double-sided YBCO thin films is a convenient way to realize large scale production and multi-component integration.
YBCO高溫超導(dǎo)薄膜在高性能微波無源器件有著良好的應(yīng)用前景,而大面積雙面薄膜的制備在滿足批量生產(chǎn)及多器件集成的同時,能夠進(jìn)一步提高微波無源器件的性能。
The superconducting MgB2 thin films were prepared on Al2O3 polycrystalline substrates by a two-step ex-situ magnesium-diffusion method with the precursor boron thin films grown by CVD from B2H6.
以高純乙硼烷(B2H6)為B源,采用化學(xué)氣相沉積(CVD)方法在多晶Al2O3襯底上沉積B薄膜,然后在Mg蒸氣中異位退火來制備MgB2超導(dǎo)薄膜。
Microwave measurements of the MgB_2 thin film;
MgB_2超導(dǎo)薄膜的微波測量